Comparison of thermal lensing effects between
single-end and double-end diffusion-bonded
Nd:YVO
4
crystals for
4
F
3/2
→
4
I
11/2
and
4
F
3/2
→
4
I
13/2
transitions
Y. T. Chang, Y. P. Huang, K. W. Su*, and Y. F. Chen
Department of Electrophysics, National Chiao Tung University, Hsinchu, Taiwan *Corresponding author: sukuanwei@mail.nctu.edu.tw
Abstract: The effective focal lengths of thermal lens in diode-end-pumped
continuous-wave Nd:YVO4 lasers for the 4F3/2→4I11/2 and 4F3/2→4I13/2
transitions were determined. The experimental results revealed that the thermal lensing effect for the 4F3/2→4I11/2 transition can be sufficiently
improved by employing a single-end diffusion-bonded Nd:YVO4 crystal
replacing a conventional Nd:YVO4 crystal. However, using a double-end
diffusion-bonded Nd:YVO4 crystal was a great improvement over a
single-end diffusion-bonded Nd:YVO4 crystal for the 4F3/2→4I13/2 transition with
stronger thermal lensing effect.
©2008 Optical Society of America
OCIS codes: (140.3480) Lasers, diode-pumped; (140.6810) Thermal effects.
References and links
1. T. Y. Fan and R. L. Byer, “Diode laser-pumped solid-state lasers,” IEEE J. Quantum Electron. 24, 895-912 (1988).
2. A. K. Cousins, “Temperature and thermal stress scaling in finite-length end-pumped laser rods,” IEEE J. Quantum Electron. 28, 1057-1069 (1992).
3. W. Koechner, Solid-State Laser Engineering, 6th ed. (Springer, New York, 2006), Chap. 7.
4. Y. F. Chen, “Design criteria for concentration optimization in scaling diode end-pumped lasers to high powers: influence of thermal fracture,” IEEE J. Quantum Electron. 35, 234-239 (1999).
5. Y. F. Chen, T. M. Huang, C. F. Kao, C. L. Wang, and S. C. Wang, “Optimization in scaling fiber-coupled laser-diode end-pumped lasers to higher power: influence of thermal effect,” IEEE J. Quantum Electron. 33, 1424-1429 (1997).
6. Y. F. Chen, C. F. Kao, T. M. Huang, C. L. Wang, and S. C. Wang, “Influence of thermal effect on output power optimization in fiber-coupled laser-diode end-pumped lasers,” IEEE J. Sel. Top. Quantum Electron. 3, 29-34 (1997).
7. W. A. Clarkson, “Thermal effects and their mitigation in end-pumped solid-state lasers,” J. Phys. D 34, 2381-2395 (2001).
8. S. C. Tidwell, J. F. Seamans, M. S. Bowers, and A. K. Cousins, “Scaling CW diode-end-pumped Nd:YAG lasers to high average powers,” IEEE J. Quantum Electron. 28, 997-1009 (1992).
9. B. Neuenschwander, R. Weber, and H. P. Weber, “Determination of the thermal lens in solid-state lasers with stable cavities,” IEEE J. Quantum Electron. 31, 1082-1087 (1995).
10. B. Ozygus, and Q. Zhang, “Thermal lens determination of end-pumped solid-state lasers using primary degeneration modes,” Appl. Phys. Lett. 71, 2590-2592 (1997).
11. F. Song, C. Zhang, X. Ding, J. J. Xu, and G. Y. Zhang, “Determination of thermal focal length and pumping radius in gain medium in laser-diode-pumped Nd:YVO4 lasers,” Appl. Phys. Lett. 81, 2145-2147 (2002).
12. S. Chénais, S. Forget, F. Druon, F. Balembois, and P. Georges, “Direct and absolute temperature mapping and heat transfer measurements in diode-end-pumped Yb:YAG,” Appl. Phys. B 79, 221-224 (2004). 13. S. Z. Fan, X. Y. Zhang, Q. P. Wang, S. T. Li, S. H. Ding, and F. F. Su, “More precise determination of
thermal lens focal length for end-pumped solid-state lasers,” Opt. Commun. 266, 620-626 (2006). 14. F. Hanson, “Improved laser performance at 946 and 473 nm from a composite Nd:Y3Al5O12 rod,” Appl.
Phys. Lett. 66, 3549-3551 (1995).
15. R. Weber, B. Neuenschwander, M. M. Donald, M. B. Roos, and H. P. Weber, “Cooling schemes for longitudinally diode laser-pumped Nd:YAG rods,” IEEE J. Quantum Electron. 34, 1046-1053 (1998).
16. M. Tsunekane, N. Taguchi, T. Kasamatsu, and H. Inaba, “Analytical and experimental studies on the characteristics of composite solid-state laser rods in diode-end-pumped geometry,” IEEE J. Sel. Top. Quantum Electron. 3, 9-18 (1997).
17. M. Tsunekane, N. Taguchi, and H. Inaba, “Efficient 946-nm laser operation of a composite Nd:YAG rod with undoped ends,” Appl. Opt. 37, 5713-5719 (1998).
18. M. Tsunekane, N. Taguchi, and H. Inaba, “Improvement of thermal effects in a diode-end-pumped, composite Tm:YAG rod with undoped ends,” Appl. Opt. 38, 1788-1791 (1999).
19. M. P. MacDonald, Th. Graf, J. E. Balmer, and H. P. Weber, “Reducing thermal lensing in diode-pumped laser rods,” Opt. Commun. 178, 383-393 (2000).
20. J.Šulc, H. Jelínková, V. Kubeček, K. Nejezchleb, and K. Blažek, “Comparison of different composite Nd:YAG rods thermal properties under diode pumping,” Proc. SPIE 4630, 128-134 (2002).
21. D. Kracht, R. Wilhelm, M. Frede, K. Dupré, and L. Ackermann, “407 W end-pumped multi-segmented Nd:YAG laser,” Opt. Express 13, 10140-10144 (2005),
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-13-25-10140.
22. Z. Zhuo, T. Li, X Li, and H. Yang, “Investigation of Nd:YVO4/YVO4 composite crystal and its laser performance pumped by a fiber coupled diode laser,” Opt. Commun. 274, 176-181 (2007).
23. Y. F. Chen, “Pump-to-mode size ratio dependence of thermal loading in diode-end-pumped solid-state lasers,” J. Opt. Soc. Am. B 17, 1835-1840 (2000).
24. M. E. Innocenzi, H. T. Yura, C. L. Fincher, and R. A. Fields, “Thermal modeling of continuous-wave end-pumped solid-state lasers,” Appl. Phys. Lett. 56, 1831-1833 (1990).
25. W. Koechner, “Thermal lensing in a Nd:YAG laser rod,” Appl. Opt. 9, 2548-2553 (1970).
1. Introduction
Diode-pumped solid-state laser has been adopted widely due to its compactness, high efficiency, and reliability [1]. Comparing with a diode-side-pumped configuration, the smaller laser beam waist, higher density of pump power, and inhomogeneous heating make thermal lensing effect become a serious problem in a diode-end-pumped configuration. The localized absorption of pump power in a laser crystal leads heat converted from pump power to
accumulate near the pumped facet of laser crystal.The nonuniform temperature distribution of
laser crystal is represented by a parabolic-logarithmic function [2]. The
temperature-dependent variation of refractive index and the end bulging effect make laser crystal act as a thermal lens [3]. Owing to the nonuniform temperature distribution the temperature gradients accrue stress that could bring thermal fracture under high pump power operation [3]. There exists a fracture-limited pump power for laser crystal that makes scaling to a higher average power be restricted [4]. For a diode-end-pumped solid-state laser, the laser performance including laser stability, maximum achievable average power, efficiency, and degradation of laser beam quality is significantly influenced by thermal lensing effect [5-7]. Therefore, promotion of laser performance can be accomplished by efficient reduction of thermal lensing
effect. End-pumped solid state laser cavity can be designed to optimize the laser performance
by determining the focal length of thermal lens. Several methods for determining the focal
length of thermal lens in diode-end-pumped laser crystal have been presented [8-13].In the
past few years, employing a composite crystal with nonabsorbing undoped end has been regarded as a promising method for cooling the laser crystal to improve the laser performance
of diode-pumped solid state laser [14-22]. With the reduction of temperature and stress, a
more uniform longitudinal temperature distribution can be generated to bring out a higher fracture-limited pump power and a higher average power.
Nd:YVO4 crystal has been seen as an excellent laser material for diode-pumped solid-state
laser due to its broad absorption bandwidth and large laser emission cross section at the
4
F3/2→4I11/2 (1064 nm) and 4F3/2→4I13/2 (1342 nm) transitions. In this work, we measured the
focal lengths of thermal lens for one conventional and two types of composite Nd:YVO4
crystal, and for the 1064- and 1342-nm transitions. One composite Nd:YVO4 crystal is
bounded with an undoped end at its pumped facet, and the other composite crystal is bounded with undoped ends at its two facets. The composite crystals were fabricated by the method of diffusion-bonding with high quality on the interface. The simple setup of continuous-wave (CW) laser was utilized to measure the focal length of thermal lens under easy operation. While the cavity length was increased to the critical cavity length, the thermal lensing effect
focal length of thermal lens can be worked out. We observed that the stronger thermal lensing
effect in Nd:YVO4 crystal for the 1342-nm transition than that for the 1064-nm transition due
to the higher thermal loading accompanying the lower conversion efficiency. The power
performance, focal lengths of thermal lens and thermal lensing effects for the three types of
Nd:YVO4 crystal for the 1064 and 1342 nm transitions will be discussed in this work.
2. Experimental setup
The experimental setup shown in Fig. 1 for measuring effective focal lengths of thermal lens
in a diode-end-pumped laser crystal is the setup of normal CW Nd:YVO4 laser. The output
coupler connected with a stepper motor can be moved in the longitudinal direction to change the cavity length. The cavity length can be changed from 2.5 to 50 cm by controlling the stepper motor. The laser crystal was pumped by an 808-nm fiber-coupled laser diode with a core diameter of 0.8 mm, a numerical aperture of 0.16, and the maximum output power was 22 W. The pump beam was reimaged into the laser crystal and the radius was about 0.4 mm. The laser crystal was wrapped in indium foil and mounted on water-cooled copper blocks.
The water temperature was maintained at 17oC. The entrance face of the 500-mm
radius-of-curvature concave front mirror was coated for antireflection at the pump wavelength of 808nm (R<0.2%) and the other face was coated for high-transmission at 808 nm (T>90%) as well as high-reflection (R>99.8%) at the lasing wavelength. In this work, we consider the
thermal lensing effect for the diode-end-pumped CW Nd:YVO4 lasers operated at 1064 and
1342 nm. The individual coatings of front mirrors and output couplers were required for achievement of different lasing wavelengths. The two flat output couplers had the reflectance of 88% at 1064 and 92% at 1342 nm used for CW 1064 and 1342 nm lasers, respectively.
laser crystal fiber coupled
laser diode focusinglens unit
front mirror
output coupler
d2
d1
Fig. 1. Experimental setup of a diode-end-pumped Nd:YVO4 CW laser for measuring the effective focal length of thermal lens in the laser crystal.
Figure 2 shows the three types of a-cut Nd:YVO4 laser crystal employed in this work. Fig.
2(a) shows a 3 mm × 3 mm × 9 mm, 0.27-at.% Nd:YVO4 crystal. Fig. 2(b) shows a 4 mm × 4
mm × 12 mm diffusion-bonded crystal called YVO4-Nd:YVO4 with single 2.7-mm-long
undoped YVO4 end at the pumped facet of 0.3-at.% active Nd:YVO4 crystal. Fig. 2(c) shows a
4 mm × 4 mm × 14 mm diffusion-bonded crystal called YVO4-Nd:YVO4-YVO4 with double
2.1-mm-long undoped YVO4 end bonded to the both facets of 0.3-at.% active Nd:YVO4
crystal. The Nd concentration was measured by the company supplying the crystals. Both sides of the three crystals were coated for antireflection at 1064 and 1342 nm (R<0.2%).
Nd:YVO4 (b)
(a) (c)
YVO4Nd:YVO4 YVO4Nd:YVO4YVO4
Fig. 2. The three types of laser crystal with different structures. (a) Conventional Nd:YVO4 crystal. (b) Diffusion-bonded Nd:YVO4 crystal with single-end at its pumped facet (YVO4-Nd:YVO4). (c) Diffusion-bonded Nd:YVO4 crystal with double-end (YVO4-Nd:YVO4-YVO4).
3. Experimental results and discussions
The laser performance of diode-end-pumped solid-state laser was strongly affected by thermal lensing effect. Figure 3 and Fig. 4 depict experimentally measured average CW power of
1064 and 1342 nm with respect to the cavity length for the three types of Nd:YVO4 crystal
under individual pump power, respectively. The sign of Pin in the Fig. 3 and Fig. 4 means the
input pump power. The average CW power was optimized at the cavity length of 2.5 cm with pump power of 8.32 and 7.61 W for 1064 and 1342 nm, respectively. In order to make sure
that the transverse mode was the TEM00 mode without high-order mode, the optimization was
done near the pump threshold. Note that while the cavity length was increased and the power was decreased rapidly, optimizing average power was not allowed. It is because the extraordinary high-order mode may compensate the power decay from thermal lensing effect.
0 10 20 30 40 50 0 1 2 3 4 5 (a)
YVO4-Nd:YVO4-YVO4
YVO4-Nd:YVO4 Nd:YVO4 Pin=10.4W Av erag e o u tp u t p o w e r at 10 64 n m (W ) Cavity length (cm) 0 10 20 30 40 50 0 2 4 6 8 10 12 (b) Pin=20.2W YVO 4-Nd:YVO4-YVO4 YVO4-Nd:YVO4 Nd:YVO4 Avera g e o u tp u t p o w e r at 1064 n m (W ) Cavity length (cm)
Fig. 3. Experimentally measured average CW output power of 1064 nm with respect to the cavity length for the three types of Nd:YVO4 laser crystal with an input pump power (a) Pin=10.4W (b) Pin=20.2W. The arrows indicate the locations of critical cavity length.
0 10 20 30 40 50 0.0 0.3 0.6 0.9 1.2 1.5 1.8 (a)
YVO4-Nd:YVO4-YVO4
YVO4-Nd:YVO4 Nd:YVO4 Pin=7.61W Avera g e o u tp u t p o w e r at 13 42 n m (W ) Cavity length (cm) 0 10 20 30 40 50 0 1 2 3 4 5 6 (b)
YVO4-Nd:YVO4-YVO4
YVO4-Nd:YVO4 Nd:YVO4 Ave rag e o u tp u t p o w e r a t 1342 n m (W ) Cavity length (cm) Pin=16.4W
Fig. 4. Experimentally measured average CW output power of 1342 nm with respect to the cavity length for the three types of Nd:YVO4 laser crystal with an input pump power (a) Pin=7.61W (b) Pin=16.4W. The arrows indicate the locations of critical cavity length.
While the cavity length was increased to a critical cavity length, the strong thermal lensing effect caused the laser cavity to become unstable. The relationships between average CW output power and cavity length are shown as Fig. 3 and Fig. 4. The maximum power at short cavity of the conventional crystal was much lower than that of the other two composite crystals mainly due to the difference in dopant concentration. The critical cavity length is determined based on unified criterion that the output power is dropped to the 70% of
maximum power at the stable (short) cavity. The corresponding focal length of thermal lens fth
(1)
where d1 and d2 are the distances from the pumped facet of laser crystal to the front mirror and
output coupler, respectively, l is the length of the laser crystal, n is the refractive index of the laser crystal, r is the radius of curvature of the front mirror. d1 was around 2.4, 1.1, and 1.6
mm for conventional Nd:YVO4, composite YVO4-Nd:YVO4, and YVO4-Nd:YVO4-YVO4,
respectively, and was fixed during the experiments.We substitute the critical cavity lengths in
terms of d1 and d2 into the Eq. (1) to get the effective focal lengths of thermal lens fth. Even
though this easy experimental method can not give an absolutely accurate fth, the relative
precision is sufficient to make comparison of thermal properties. The experimentally obtained
fth are plotted as symbols in Fig. 5. According to the theoretical thermal modeling of CW
end-pumped solid-state laser presented by Innocenzi et al., the effective focal length can be approximately expressed by [24]
(2)
where K is the thermal conductivity, ωp is the pump-beam radius in the active medium in the
unit of mm, ξ is the fractional thermal loading, Pin is the pump power in the unit of watt (W),
(dn/dT) is the thermal-optical coefficient of n, α is the absorption coefficient, la is the length
of the active medium, C is a proportional constant in the unit of W/mm. Because the thermal
conductivity of YVO4 in the b- and c-axis of 5.1 and 5.23 W/mK are very close, respectively,
it can be seen as a radial symmetry thermal model [4]. The Innocenzi model for rod-type crystal is available here. The Eq. (2) is used to fit the experimental data and the theoretical fitted curves with the approximate corresponding constants C are depicted in Fig. 5.
4 8 12 16 20 24 0 100 200 300 400 500 YVO4-Nd:YVO4-YVO4 YVO4-Nd:YVO4 Nd:YVO4 E ff ect ive f o cal len g th o f t h er m a l len s ( c m )
Input pump power (W) (a) λ = 1064 nm 4 8 12 16 20 0 40 80 120 160 λ = 1342 nm YVO4-Nd:YVO4-YVO4 YVO4-Nd:YVO4 Nd:YVO4 E ff e ct iv e f o c a l len g th o f t h e rm a l l e n s ( c m )
Input pump power (W) (b)
Fig. 5. The relationship between the effective focal length of thermal lens and the input pump power for three types of Nd:YVO4 crystal operated at (a) 1064 (b) 1342 nm. The symbols represent experimental data and the curves are theoretical fitted results.
The constants C of the conventional Nd:YVO4, composite YVO4-Nd:YVO4, and YVO4
-Nd:YVO4-YVO4 for the 1064-nm transition are 4.9×104, 11×104, and 11×104 W/mm,
respectively. The constants C of the conventional Nd:YVO4, composite YVO4-Nd:YVO4, and
YVO4-Nd:YVO4-YVO4 for the 1342-nm transition are 2.1×104, 2.5×104, and 3.4×104 W/mm,
respectively. The bigger constant C which represents the longer focal length of thermal lens
means the weaker thermal lensing effect. The increase of the pump power enhanced the
thermal lensing effect. With the equal pump power, the focal length of thermal lens for CW 1342-nm laser was shorter than that for CW 1064-nm laser due to the higher thermal loading.
in p a in p th P C l dT dn P K f 2 2 ) ( exp 1 1 ) / ( ω α ξ ω π = ⎥ ⎦ ⎤ ⎢ ⎣ ⎡ − − = 1 2 1 1 1 1 1 d r n l d fth − − ⎟ ⎠ ⎞ ⎜ ⎝ ⎛ − + =
The higher thermal loading accompanying the lower conversion efficiency was mainly attributed to the higher quantum defect for the longer laser wavelength.
According to the above-mentioned constants C, it is proven that both the focal lengths of
thermal lens in the YVO4-Nd:YVO4 and YVO4-Nd:YVO4-YVO4 were increased by nearly
2.2-times that in the conventional Nd:YVO4 for the 1064-nm transition. The focal lengths of
thermal lens in the YVO4-Nd:YVO4 and YVO4-Nd:YVO4-YVO4 were increased by nearly 1.2
and 1.6-times that in the conventional Nd:YVO4 for the 1342-nm transition, respectively.
Even though the ability of thermal diffusivity in a laser crystal with bigger cross section was
inferior [16, 25], the focal lengths of thermal lens in the two composite Nd:YVO4 crystals
were longer than that in the conventional Nd:YVO4 crystal. In addition, we discuss the
influence of different dopant concentration and the length of active medium on the thermal
lens. The absorption coefficient α for a typical laser diode with the center wavelength of 808
nm is expressed by [4]
(3)
where Nd is the Nd dopant concentration in the unit of %. The values of αl were 4.86, 5.58,
and 5.88 for the conventional Nd:YVO4, the composite YVO4-Nd:YVO4, and YVO4
-Nd:YVO4-YVO4, respectively. According to the Eq. (2), the bigger value of αl represents the
shorter focal length of thermal lens. But the differences in the value of [1-exp(-αl)]-1 between the three crystals was below 0.5 % and could be ignored. Further, the influence of different cross section on the thermal diffusivity was small for edge cooling system. Even we consider the influence, the conventional crystal with small cross section would have better thermal diffusivity and the conclusion does not be changed. Therefore, it is seen that the improvement
of thermal lensing effect contributed by employing the two diffusion-bonded Nd:YVO4
crystals greatly overcame the disadvantage of the bigger cross section.
The experimental results revealed that the thermal lensing effect in the YVO4-Nd:YVO4
was nearly equal to that in the YVO4-Nd:YVO4-YVO4 for the highest efficient 1064-nm
transition. Therefore only single undoped end at the pumped facet of laser crystal was sufficient for improving the thermal lensing effect to increase the effective focal length of
thermal lens to nearly 2.2 times that of the conventional Nd:YVO4 crystal for CW 1064-nm
laser. However, the improvement in thermal lensing effect of the YVO4-Nd:YVO4-YVO4
noticeably outperformed that of the YVO4-Nd:YVO4 for the 1342-nm transition. As a result of
the stronger thermal lensing effect for the 1342-nm transition, the double undoped ends bonded to the both facets of active medium were essential for assisting thermal diffusing to increase the effective focal length of thermal lens to nearly 1.6 times that of the conventional Nd:YVO4 crystal.
4. Conclusion
The comparison of thermal lensing effects between diffusion-bonded YVO4-Nd:YVO4 and
YVO4-Nd:YVO4-YVO4 crystals with single- and double-end, respectively, was demonstrated
by measuring the effective focal lengths of thermal lens. The both types of diffusion-bonded
crystal could improve the thermal lensing effects of conventional Nd:YVO4 crystal. The
YVO4-Nd:YVO4 was capable of accomplishing the improvement in thermal lensing effect of
YVO4-Nd:YVO4-YVO4 for the 1064-nm transition. However, the improvement of YVO4
-Nd:YVO4-YVO4 remarkably towered over that of YVO4-Nd:YVO4 for the 1342-nm transition
with stronger thermal lensing effect. Therefore YVO4-Nd:YVO4 and YVO4-Nd:YVO4-YVO4
crystals can serve as promising substitutes for a conventional Nd:YVO4 crystal to reduce
thermal lensing effect and scale to a higher average power of diode-end-pumped CW
Nd:YVO4 lasers operated at 1064 and 1342 nm, respectively.
Acknowledgments
The authors thank the National Science Council for their financial support of this research under Contract No. NSC-95-2112-M-009-041-MY2.
) (mm 2 -1 d N ⋅ = α
![TraditionalMLCalgorithmsmainlytacklethebatchMLCproblem,wheretheinputdataarepresentedinabatch[24,28].Nevertheless,inmanyMLCapplicationssuchase-mailcategorization[22],multi-labelexamplesarriveasastream.Onlineanalysisistherefore dimensionreducermotivatedbyma](data:image/gif;base64,R0lGODlhAQABAIAAAP///wAAACH5BAEAAAAALAAAAAABAAEAAAICRAEAOw==)