Leached components from dental composite in oral

simulating fluids and then resultant composite

strengths.

黃豪銘

Lee SY;Huang HM;Lin CY and Shih YH

Abstract

The aim of this study was to analyse the leached moieties of dental composites after storage in ethanol and organic acids of plaque and further evaluate the resultant effect on the diametral tensile strength (DTS) of the composites. Three commercial composites were used: Bis-GMA-based Z100, Bis-GMA/UDMA-based Heliomolar, and Bis-MPEPP-based Marathon One. The solutions used were: 99.9% acetic acid, 99% propionic acid and 75% ethanol. Specimens (4 mm diam. x 2 mm thick) were stored at 37 degrees C in 3 mL of solution for up to 30 days. Gas

chromatography/mass spectrometry was used to characterize the leached moieties and DTS of the specimens after immersion was evaluated. Data were analysed using ANOVA and Tukey LSD test. The eluted substances were not all the same in different solutions and composites but mostly increased with immersion time, and included diluents (TEGDMA and decamethacrylate) and some additives, such as an

ultra-violet stabilizer (TINUVINP), plasticizers (dicyclohexyl phthalate and bis(2-ethylhexyl) phthalate), initiator (triphenyl stibine), coupling agent

(gamma-methacryloxypropyl trimethoxysilane), and phenyl benzoate. The chief polymerizing monomers were not found. More kinds of components were found in the acetic acid and ethanol groups studied. The fewest kinds and quantities of leached moieties were found for Bis-GMA specimens and then Bis-GMA/UDMA ones, most of which are diluent agents. Bis-MPEPP specimens leached the most

substances, which were composed mostly of a short phenyl group chain structure. The BisGMA composite showed the highest DTS (54.8 +/- 5.7 MPa), which was not greatly affected by the length of storage. Bis-GMA/UDMA (36.2 +/- 6.8 MPa) and Bis-MPEPP (26.1 +/- 4.5 MPa) composites were significantly reduced (P < 0.05) after 30 days storage in the ethanol (35-50%), in the propionic acid (25-30%), and in the acetic acid (40-60%). Irreversible processes such as the leaching of

components occur in fluids simulating an oral environment, which may contribute to irreversible material degradation, especially for non-Bis-GMA-based composites.

參考文獻

相關文件

Therefore, the aim of the present study was to explore the correlation between the severity of RTG and endothelial cell injury in local tissues in a rat model and to identify

Aim: The aim of this study is to investigate the prevalence of medical con- ditions and medications used by patients accessing emergency dental care at Manchester Dental

Therefore, the aim of this study was to obtain, explore and interpret a deeper understanding of patients’ experiences and perspectives after they have experi- enced dental

This is a retrospective study of 1521 biopsy request forms of specimens submitted for histopathological examination to the Department of Oral Pathology and Medicine, Dental

Background: The purpose of this study was to evaluate the immunohistochemical expression of NF-κB and IL-6 in oral premalignant and malignant lesions and to

The aim of this study was to evaluate the volumetric accuracy and reliability of cone beam computed tomography (CBCT)-based tooth segmentation using 4 different CBCT

The aim of the present study was to study the cytological spectrum of lesions of the oral cavity and salivary glands, to evaluate the role of fine needle aspiration cytology as

The aim of this study was to investigate, through a prospective clinical study, the prevalence and characteristics of oral lichen planus (OLP) and lichenoid lesions (OLL) in