The Study of Hot Embossing PTFE to Function of Faucet Washer 吳守禮、吳政憲
E-mail: [email protected]
ABSTRACT
The development of faucet and tap water have much closed relationship. For the past years,the shape material and function of the faucet is much improved, farther more, it becomes a guide of civilization life. Today the delicate pottery axle center faucet durability is much improved. This research mainly conferred into the less cause of abrasion in condition hot compressive the PTFE thin being placed on NBR stop washer makes, enhance the using efficiency. How to improve the traditional NBR rubber to advance the mechanism substance,replace the convenient water-proof washer under the pressure of competition of pottery axle center and electronically sensor faucet. Therefore this research put an ego into the hot-press process argument the hot-press temperature, and vulcanization time, and replace NBR water-proof washer with the excellent mechanical quality of anti-abrasion, delay-aging of PTFE. In according to ASTM standard to put vulcanized test paper under the test of being aged,stretched, abraded, and take the water-proof washer ameliorated by the hot pressed into real efficient test, to with the best argument verify the efficiency of the ameliorant.
Keywords : aging，vulcanization，hot pressing shape
Table of Contents
封面內頁 簽名頁 授權書...iii 中文摘要...iv 英文摘
要...v 誌謝...vi 目錄...vii 圖目 錄...x 表目錄...xiv 第一章 序 論 1.1 前
言...1 1.2 龍頭的發展...1 1.3 研究動機...2 1.4 研究方 法...3 1.5 本文目標...3 第二章 實驗設計之建構 2.1 實驗材
料...8 2.2 文獻探討...10 2.3 熱壓真空成型機...16 2.4 模具 設計...17 2.5 動態熱壓成型...18 2.6 實驗儀器...20 2.7 接 著劑...23 第三章 實驗方法與步驟 3.1 NBR硫化...33 3.2 高分子熱壓成型製 程...34 3.3 老化試驗...36 3.4 拉伸試驗...37 3.5 磨耗試 驗...38 第四章 實驗結果與討論 4.1 止水墊圈成型探討...49 4.2 硫化對PTFE接著成 型之影響...52 4.3 硫化橡膠老化對PTFE熱壓於NBR之影響...53 4.4 摩擦面材料分
析...54 4.5 磨耗行為探討...56 第五章 結論與建議 6.1 結
論...82 6.2 建議...83 參考文獻...84 REFERENCES
[1] 張哲豪，”流體微熱壓製成開發研究”，台灣大學博士論文， （2004）。
[2] 林威宇，”動態壓力控制對微結構熱壓特性的影響暨加工過 程中聚丙烯的結晶特性的初步探討”，交通大學碩士論文， （2005）。
[3] 郭.彰，”微結構熱壓成型之製程研究”，大葉大學碩士論 文，（2005）。
[4] 陳劉旺、丁金超， ”高分子加工”，高立圖書公司， （1999）。
[5] 張志純，”塑膠大全”，徐氏出版社，（2001）。
[6] 鄧建民，”橡膠大全”，徐氏出版社，（2002）。
[7] 謝立生，”橡膠配方手冊”，高分子工業雜誌社，（1995）。
[8] 何經、陳金順，”高分子加工”，台灣復文公司，（1995）。
[9] 彭耀寰，”高分子材料”，大中國出版社，（1990）。
[10] 賴耿陽，”塑膠成形品質研究”，復漢出版社，（2000）。
[11] 伊藤公正，”塑膠材料手冊”，台灣文源書局有限公司，（1999）。
[12] 黃立寧，”PTFE/Nafion-TEOS(tetraethoxysilane)複合膜的製備及性能研究”，元智大學碩士論文， （2003）。
[13] 李丞欽，” 滑道用潤滑油於低壓低速下之摩擦特性研究”，台灣大學碩士論文，（2000）。
[14] 陳世春，劉守一，”塑膠材料潤滑性質”，復漢出版社， （1991）。
[15] 廖明隆， ”合成橡膠”，鼎文書局，（2000）。 -84- [16] 賴耿陽，”最新橡膠材料實務”，復漢出版社，（2001）。
[17] M. L. Shaw,P. H. S. Tsang and S. K. Rhee, ” Study of the friction and wear behavior of aluminum composites sliding against polymer composites”,Wear of Materials:Inter-national Conference on Wear of Materials,1（1991）,167-175.
[18] J. W. M. Mens and A. W. J. de Gee, ” Friction and wear behavior of 18 polymers in contact with steel in environments of air and water”, Wear of Materials: InternationalConference on Wear of Materials,1（1991）,563-570.
[19] K. Tanaka and Y. Uchiyama, ”The Mechanism of Wear Polytera- fluoro ethylene”,Wear,23(1977),153-172.
[20] Zhao-Zhu Zhang,Wei-Chang Shen,Wei-Min Liu,Qun-Ji Xue and Tong-Sheng Li, ”Tribological Properties of Polytertra- fluoroethylene-Based Composites in Different Lubricant M edia”,Wear,196（1996）,164-170.
[21] Zhao-Zhu Zhang, Qun-Ji Xue, Wei-Min Liu and Wei-Chang Shen, ” Friction and Wear Properties of Metal Powder fil led PTFE Composites under Oil-Lubricated Conditions”, Wear,210（1997）,151-156.
[22] Zhao-Zhu Zhang, Qun-Ji Xue, Wei-Min Liu and Wei-Chang Shen, ” Friction and Wear Characteristics of Copper and Its Compound-Filled PTFE Composites under Oil-Lubricat-ed Con ditions”,J.of Applied Polymer Science,70（1998）.
[23] 許評順，”高分子PTFE押出流變特性量測系統之建立”， 中原大學碩士論文，（2003）。
[24] 高振育，”PTFE表面改質之研究與應用”，中原大學博士論文，（1998）。
[25] 胡德，”高分子物理與機械性質上、下”，渤海堂公司，（1990）。
[26] 邱顯堂，”高分子物性”，明文書局股份有限公司，（1998）。
[27] E.Marui,H.Endo, M. Hashimoto and S. kato, ”Some conside-ration ofSlideway Friction Characteristics by ObservingStick- Slip Vibration
”,Tribology Interational, 29,251-262(1996).
[28] Jin Tae Kim, Keun Byoung Yoon, Choon-Gi Choi, ” Passive Alignment Method of Polymer PLC Devices by Hot Embossing Technique
”,IEEE Photonics Technology Letters,vol.16, no.7, pp.1664-1666(2004).
[29] H. Becker, U. Heim, ” Hot embossing as a method for he fabrication of Polymer high aspect ratio structures”， Sensors and Actuators, pp.
130-135(2000).
[30] M. Heckele, W. Bacher, K.D. Muller, ”Hot embossing the molding technique for plastic microstructures”, Microsyst- em Technology 4, pp.
122-124(1998).
[31] L.J. Heyderman, C. Schift, J. David, T. Gobrecht, L.J. Schweizer ”Flow behavior of thin polymer films used for-hot embossing lithography
”, Microelectronic Engineering54, pp.229-245(2000).
[32] 蘇品書，”塑膠複合材料”，復漢出版社，（1999）。
[33] 彭志剛，”以電漿處理聚四氟乙烯表面改質之研究”，中央大學碩士論文，（2003）。
[34] 周瑞樞，”聚縮醛/聚四氯乙烯複合材料界面改質之研究”，大同大學碩士論文，（1996）。
[35] 吳逸人，”PTFE膜光接枝表面改質及特性研究”，成功大學碩士論文，（1995）。
[36] 張簡四續，”複合無電鍍鎳/鐵氟龍碳纖維複合材料電磁遮蔽及機械性質之研究”，大同大學 碩士論文，（1997）。