最後，針對本實驗的結果，可以提出以下兩點作為未來研究以及改善方向：
1. 由實驗結果可以發現，抗高溫氧化鍍層與底材間熱膨脹係數的差異會影響鍍 層破裂行為進而影響後續處理以及抗蝕效果，且後續氧化傾向在該區域發生。
故若能調整鍍層熱膨脹係數，使其接近底材，將對於抗高溫氧化效果有明顯 的提升。
2. 由實驗結果可以發現到，在矽烷鈍化皮膜與底材交界處可以發現到氧化鋁的 擴散障蔽保護層，此現象在superalloy 玻璃抗高溫氧化鍍層的研究也有被提 到[66]，該擴散層主要是由於玻璃鍍層降低底材表接合處氧壓導致。擴散障 蔽保護層對於抗高溫氧化的影響，以及如何增加或是改善該擴散層的性質可 為未來研究方向。
參考文獻
[1] Karbasian, H. and A.E. Tekkaya, A review on hot stamping. Journal of Materials Processing Technology, 2010. 210(15): p. 2103-2118.
[2] Naderi, M., Hot stamping of ultra high strength steels. Doctoral Theses, RWTH Aachen, 2007.
[3] J. E. Morral, J.B. Cameron, Boron hardenability mechanisms, the Metallurgical Society of the A.I.M.E., 1980.
[4] J. E. Morral, J. B. Cameron, Metallurgical and Materials Transactions A, 1977.
[5] P. Maitrepierre, D. Thivellier, J. Roves-Vernis, D. Rousseau, R. Tricot, Hardenability concepts with application to steel, A.I.M.E., Warrendale, USA,1978.
[6] Fan, D.W. and B.C. De Cooman, State-of-the-Knowledge on Coating Systems for Hot Stamped Parts. steel research international, 2012. 83(5): p. 412-433.
[7] Liu, H., et al., Enhanced mechanical properties of a hot stamped advanced high-strength steel treated by quenching and partitioning process. Scripta Materialia, 2011. 64(8): p. 749-752.
[8] Fan, D.W., et al., Influence of Isothermal Deformation Conditions on The Mechanical Properties of 22MnB5 HPF Steel. steel research international, 2010.
81(4): p. 292-298.
[9] Merklein, M. and J. Lechler, Investigation of the thermo-mechanical properties of hot stamping steels. Journal of Materials Processing Technology, 2006. 177(1-3):
p. 452-455.
[10] Bariani, P.F., et al., Testing formability in the hot stamping of HSS. CIRP Annals, 2008. 57(1): p. 265-268.
[11] Drillet, P., Spehner, D., Kefferstein, R., Patent WO08053273, 2008.
[12] Richards, R.W., et al., Metallurgy of continuous hot dip aluminizing. International
Materials Reviews, 1994. 39(5): p. 191-212.
[13] Suehiro, M., Kusumi, K., Miyakoshi, T., Maki, J., Ohgami, M., Properties of aluminium-coated steels for hot-forming. Nippon Steel Technical Report, 2003. 88:
p. 16–21.
[14] Takagi, K., Nakanishi, E., Yoshida, J., Patent EP1380666, 2004.
[15] Allely, C., Petitjean, J., Vietoris, T., 3rd International conference on hot sheet metal forming of high-performance steel, 2011, p. 153–160.
[16] Schwartz, R., Lehmann, H., 2nd International conference on hot sheet metal forming of high-performance steel, 2009, p. 323–330.
[17] Kondratiuk, J., et al., Zinc coatings for hot sheet metal forming: Comparison of phase evolution and microstructure during heat treatment. Surface and Coatings Technology, 2011. 205(17-18): p. 4141-4153.
[18] Goedicke, S., Sepeur, S., Breyer, C., Asia steel international conference, 2009.
[19] Marder, A.R., The metallurgy of zinc-coated steel, Progress in Materials Science, 2000. 45:p. 191–271.
[20] Shibli, S.M.A., B.N. Meena, and R. Remya, A review on recent approaches in the field of hot dip zinc galvanizing process. Surface and Coatings Technology, 2015.
262: p. 210-215.
[21] Faderl, J., 2nd International conference on hot sheet metal forming of high-performance steel, 2009, p. 283–291.
[22] Autengruber, R., et al., Surface and Coating Analysis of Press-Hardened Hot-Dip Galvanized Steel Sheet. steel research international, 2012. 83(11): p. 1005-1011.
[23] Imai, K., Yoshikawa, Y., Toki, T., Nishibata, T., Uematsu, K., Uchihara, M., Takayama, T., Properties of hot stamped galvannealed steel sheet, South East Asia Iron Steel Inst. Q., 2005. 34(4):p. 47–53.
[24] Fleischanderl, M., Kolnberger, S., Faderl, J., Landl, G., Raab, A. E., Brandstatter, W., Patent US20070256808, 2007.
[25] Yoshikawa, Y., Imai, K., Fukui, K., Toki, T., Sudo, S., Obayashi, A., Ichikawa, M., Patent EP1630244, 2009.
[26] Lee, C.W., Fan, D.W., Lee, S.J., B. C. DeCooman, 8th International conference on zinc and zinc alloy coated steel sheet, 2011, p. 327–334.
[27] D. F. Anthrop, A. W. Searcy, Sublimation and Thermodynamic Properties of Zinc Oxide. Journal of Physical Chemistry, 1964. 68(8):p. 2335–2342.
[28] Lee, C.W., et al., Liquid-Metal-Induced Embrittlement of Zn-Coated Hot Stamping Steel. Metallurgical and Materials Transactions A, 2012. 43(13): p. 5122-5127.
[29] Lee, C.W., Choi, W.S., Cho, Y.R., B.C. De Cooman, Surface Oxide Formation during Rapid Heating of Zn coated press hardening steel, ISIJ International., 2014.
54(10):p. 2364-2368.
[30] Akioka, K., Nishibata, T., Imai, K., Takayama, T., Nakata, M., Fujimoto, H., Kojima, N., Matsumoto, M., 8th International conference on zinc and zinc alloy coated steel sheet, 2011,p. 363–369.
[31] Autengruber, R., G. Luckeneder, and A.W. Hassel, Corrosion of press-hardened galvanized steel. Corrosion Science, 2012. 63: p. 12-19.
[32] 孫秋霞，材料腐蝕與防護，冶金工業出版社，2001.
[33] David, R. G., Introduction to the Thermodynamics of Materials, Fifth Edition, 2008.
[34] Neil Birks, Gerald H. Meier, Frederick S. Pettit, Introduction to the High Temperature Oxidation of Metals, Second Edition, 2006.
[35] C.H. Xu, W. Gao, Pilling-Bedworth ratio for oxidation of alloys. Material Research Innovations, 2000. 3(4):p. 231-235.
[36] N.B. Pilling and R.E. Bedworth, The Oxidation of Metals at High Temperatures, Journal of the Institute of Metals, 1923. 29:p.529.
[37] M. Pourbaix, Atlas of electrochemical equilibria in aqueous solutions, Second edition, 1966.
[38] Material Safety Data Sheet of Chromium(VI) oxide [39] Material Safety Data Sheet of Tetraethyl orthosilicate
[40] Material Safety Data Sheet of (3-Glycidyloxypropyl)trimethoxysilane
[41] C. Brinker, A. Hurd, P. Schunk, G. Frye, Review of Sol–Gel Thin Film Formation, Journal of Non-Crystalline Solids, 1992. 148:p. 424–436.
[42] A. C. Pierre, Introduction to Sol–Gel Processing, 1998.
[43] 蘇香宇，鍍鋅鋼板之磷酸鹽鈍化處理及溶膠凝膠法鈍化處理，台灣大學博士 論文，中華民國103年7月
[44] Alothman, Z., A Review: Fundamental Aspects of Silicate Mesoporous Materials.
Materials, 2012. 5(12): p. 2874-2902.
[45] C.J. Brinker, G.W. Scherer, The Physics and Chemistry of Sol-Gel Processing, First edition, 1990.
[46] 陳德順，熱浸鍍鋅鋼板溶膠凝膠鈍化處理之研究，台灣大學碩士論文，中華 民國105年7月
[47] Chvedov, D. and E.L.B. Logan, Surface charge properties of oxides and hydroxides formed on metal substrates determined by contact angle titration. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2004. 240(1-3): p. 211-223.
[48] Vittoz, C., M. Mantel, and J.C. Joud, Wettability of Metallic Oxides—Application to Stainless Stell Acid-Base Properties. The Journal of Adhesion, 1998. 67(1-4): p.
347-358.
[49] Li, B. and B.E. Logan, Bacterial adhesion to glass and metal-oxide surfaces.
Colloids Surf B Biointerfaces, 2004. 36(2): p. 81-90.
[50] M. Guglielmi, Sol-Gel Coatings on Metals, Journal of Sol-Gel Science and Technology, 1997. 8: p. 443-449.
[51] J. Uchida, K. Kawakami, S. Sato, The Development of Thinner Chromium-free Chemical for Zinc Plating, Nihon Parkerizing Technical Report, 2012.
[52] Nikrooz, B., M. Zandrahimi, and H. Ebrahimifar, High temperature oxidation resistance and corrosion properties of dip coated silica coating by sol gel method on stainless steel. Journal of Sol-Gel Science and Technology, 2012. 63(3): p. 286-293.
[53] Tsai, C.-Y., et al., Effect of Mg2+ on the microstructure and corrosion resistance of the phosphate conversion coating on hot-dip galvanized sheet steel. Corrosion Science, 2010. 52(12): p. 3907-3916.
[54] Tsai, C.-Y., et al., A roll coating tungstate passivation treatment for hot-dip galvanized sheet steel. Surface and Coatings Technology, 2011. 205(21-22): p.
5124-5129.
[55] Tsai, C.-Y., et al., A two-step roll coating phosphate/molybdate passivation treatment for hot-dip galvanized steel sheet. Corrosion Science, 2010. 52(10): p.
3385-3393.
[56] K. Ishizuka, H. Shindo, K. Hayashi, Phosphate-treated galvanized steel sheet excellent in corrosion resistance and paintability. Patent US 6,596,414 B1, 2003.
[57] C. J. Brinker, G. C. Frye, A. J. Hurd, C. S. Ashley, Fundamentals of sol-gel dip coating. Thin Solid Films, 1991. 201(1): p. 97-108.
[58] L.E. Scriven, in C. J. Brinker, D. E. Clark and D. R. Ulrich (eds.), Better Ceramics Through Chemistry 111, Materials Research Society, 1988. p. 717-729.
[59] L. Landau, B. Levich, Dragging of a Liquid by a Moving Plate, Dynamics of
Curved Fronts, 1988. p. 141–153
[60] M. Faustini, B. Louis, P. A. Albouy, M. Kuemmel, D. Grosso, Preparation of Sol-Gel Films by Dip-Coating in Extreme Conditions. The Journal of Physical Chemistry, 2010. 114: p. 7637–7645.
[61] Zhang, X.G. and Bravo, I.C., Electrochemical Stripping of Galvannealed Coatings on Steel. Corrosion Science, 1994. 50: p. 308-317.
[62] Schlesinger, M. and Paunovic, M., Modern Electroplating, Fifth Edition, 2014.
[63] 林克駿，雙相鋼鋼板熱浸鍍鋅鍍層合金化與高溫氧化行為之研究，台灣大學 博士論文，中華民國103年7月
[64] E. McCafferty, Introduction to Corrosion Science, 2009.
[65] 李言祥，材料加工原理，清華大學出版社，2005.
[66] M. Chen, M. Shen, S. Zhu, F. Wang, X. Wang, Effect of sand blasting and glass matrix composite coating on oxidation resistance of a nickel-based superalloy at 1000℃. Corros. Science, 2013. 73: p. 331–341.